MDL | MFCD00011104 |
InChIKey | VTHJTEIRLNZDEV-UHFFFAOYSA-L |
Inchi | 1S/Mg.2H2O/h;2*1H2/q+2;;/p-2 |
SMILES | [Mg+2].[OH-].[OH-] |
LogP | -0.35360 |
PSA | 40.46000 |
Merck | 14,5670 |
水溶性 | 0.9 mg/100 mL (18 ºC) |
沸点 | 100ºC at 760mmHg |
熔点 | 350 °C (lit.) |
闪点 | will not burn |
溶解度 | 5 M HCl: 0.1 M, clear, yellow |
颜色与性状 | 无色结晶,属六方晶系。系六角形或无定形片状结晶,无气味 |
稳定性 | Stable. |
溶解性 | 溶于稀酸和铵盐溶液,几乎不溶于水和醇。 |
敏感性 | Air Sensitive |
密度 | 2,36 g/cm3 |
外观性状 | 无色六方柱晶体 |
精确分子量 | 57.99050 |
氢键供体数量 | 0 |
氢键受体数量 | 2 |
可旋转化学键数量 | 0 |
同位素质量 | 57.991 |
重原子数量 | 3 |
复杂度 | 0 |
同位素原子数量 | 0 |
确定原子立构中心数量 | 0 |
不确定原子立构中心数量 | 0 |
确定化学键立构中心数量 | 0 |
不确定化学键立构中心数量 | 0 |
共价键单元数量 | 3 |
疏水参数计算参考值(XlogP) | 无 |
互变异构体数量 | 无 |
表面电荷 | 0 |
拓扑分子极性表面积 | 2 |
符号: |
GHS07
![]() |
RTECS号 | OM3570000 |
WGK Germany | nwg |
安全说明 | S26; S36; S37/39 |
风险术语 | R36/37/38 |
危险品标志 |
Xi
![]() |
危险品运输编号 | NONH for all modes of transport |
危害声明 | H315,H319,H335 |
警示性声明 | P261,P305+P351+P338 |
储存条件 | Store in a cool, dry, well-ventilated area away from incompatible substances. Keep containers tightly closed. |
危险类别码 | 36/37/38 |
信号词 | Warning |
TSCA | Yes |
FLUKA BRAND F CODES | 3-9 |
EINECS | 215-170-3 |
EINECS | 215-170-3 |
海关编码 | 28161000 |
用途 | 1、用作分析试剂,也用于制药工业 2、主要用作阻燃剂 3、在医药上用作抗酸剂和缓泻剂,还可用于制糖和氧化镁等 4、氢氧化镁是塑料、橡胶制品优良的阻燃剂。在环保方面作为烟道气脱硫剂,可代替烧碱和石灰作为含酸废水的中和剂。亦用作油品添加剂,起到防腐和脱硫作用。另外,还可用于电子行业、医药、砂糖的精制,作保温材料以及制造其他镁盐产品。 5、糖的精炼,制药工业。 |
生产方法 | 1、卤水一石灰法将预先经过净化精制处理的卤水和经消化除渣处理的石灰制成的石灰乳在沉淀槽内进行沉淀反应,在得到的料浆中加入絮凝剂,充分混合后,进入沉降槽进行分离,再经过滤、洗涤、烘干、粉碎,制得氢氧化镁成品。其 MgCl2+Ca(OH)2→CaCl2+Mg(OH)2.
2、卤水-氨水法以经净化处理除去硫酸盐、二氧化碳、少量硼等杂质的卤水为原料,以氨水作为沉淀剂在反应釜中进行沉淀反应,在反应前投入一定量的晶种,进行充分搅拌。卤水与氨水的比例为1:(0.9~0.93),温度控制在40℃。反应终了后添加絮凝剂,沉淀物经过滤后,洗涤、烘干、粉碎,制得氢氧化镁成品。其 3、菱苦土-盐酸-氨水法菱镁矿石与无烟煤或焦炭在竖窑内煅烧,生成氧化镁和二氧化碳。苦土粉用水调成浆状后与规定浓度的盐酸反应制备氯化镁溶液。其 氯化镁溶液与一定浓度的氨水在反应器中进行反应,生成物经洗涤、沉降、过滤分离、干燥、粉碎,得到氢氧化镁产品。根据需要可添加表面处理剂进行表面处理。 |
1.
Effect of different parameters on caustic magnesia hydration and magnesium hydroxide rheology: a review
Ghada Bassioni,Reham Farid,Mayar Mohamed,Rawia M. Hammouda,Fritz E. Kühn Mater. Adv. 2021 2 6519
2.
Biodegradable poly(l-lactide) composites by oligolactide-grafted magnesium hydroxide for mechanical reinforcement and reduced inflammation
Chang Hun Kum,Youngjin Cho,Yoon Ki Joung,Jiyeon Choi,Kwideok Park,Seong Ho Seo,Yong Seek Park,Dong Jun Ahn,Dong Keun Han J. Mater. Chem. B 2013 1 2764
3.
Waste to resource: preparation of an efficient adsorbent and its sustainable utilization in flame retardant polyurethane composites
Bei Tu,Keqing Zhou,Qianqian Zhou,Kaili Gong,Dongtao Hu RSC Adv. 2021 11 9942
4.
Biocompatible and functional inorganic magnesium ceramic particles for biomedical applications
Tarek M. Bedair,Yun Heo,Jungju Ryu,Hanan M. Bedair,Wooram Park,Dong Keun Han Biomater. Sci. 2021 9 1903
5.
Direct bottom-up synthesis of size-controlled monodispersed single-layer magnesium hydroxide nanosheets modified with tripodal ligands
Keisuke Muramatsu,Yuya Kamiusuki,Yoshiyuki Kuroda,Hiroaki Wada,Atsushi Shimojima,Kazuyuki Kuroda Dalton Trans. 2021 50 3121
6.
Recent progress in the synthesis of nanostructured magnesium hydroxide
Giulia Balducci,Laura Bravo Diaz,Duncan H. Gregory CrystEngComm 2017 19 6067
7.
In situ synthesis of magnesium hydroxides modified with tripodal ligands in an organic medium
Keisuke Muramatsu,Yoshiyuki Kuroda,Hiroaki Wada,Atsushi Shimojima,Kazuyuki Kuroda Dalton Trans. 2018 47 3074
8.
Magnesium hydroxide nanoplates: a pH-responsive platform for hydrophobic anticancer drug delivery
Mingyi Guo,Faheem Muhammad,Aifei Wang,Wenxiu Qi,Nan Wang,Yingjie Guo,Yen Wei,Guangshan Zhu J. Mater. Chem. B 2013 1 5273
9.
Magnesium hydroxide nanoplates: a pH-responsive platform for hydrophobic anticancer drug delivery
Mingyi Guo,Faheem Muhammad,Aifei Wang,Wenxiu Qi,Nan Wang,Yingjie Guo,Yen Wei,Guangshan Zhu J. Mater. Chem. B 2013 1 5273
10.
Enhanced removal of cephalosporin based antibiotics (CBA) from water by one-pot electrosynthesized Mg(OH)2: a combined theoretical and experimental study to pilot scale
Aarthi Pandiarajan,Ramakrishnan Kamaraj,Subramanyan Vasudevan New J. Chem. 2017 41 4518
Beilstein | 215-170-3 |
毒性
ADI不作限制性规定(FAO/WHO,2001)。
GRAS(FDA,§182.1428,2000)。
氢氧化镁鉴别试验
用稀盐酸试液(TS-117)配制5%的试样液,其镁试验(IT-21)呈阳性。
氢氧化镁含量分析
精确称取预经105℃干燥2h的试样约400mg,移入锥形烧瓶中。加lmol/L硫酸25.0ml,待完全溶解后,加甲基红试液(TS-149)数滴,用1mol/L****滴定过量的酸。由所耗1mol/L硫酸的体积减去与所取试样中氧化钙含量(见质量指标)相当的1mol/L硫酸体积,其差即为相当于所取试样中Mg(OH)2含量的1mol/L硫酸体积。每Ml,1mol/L硫酸相当于Mg(OH)2 29.16mg或CaO28.04mg。
使用限量
FAO/WHO(1984):可可粉及含糖可可粉、可可豆粉、可可液块及可可油饼,5g/kg(以无脂可可计,K2CO3计)。